Investigations on the thickness dependent structural, morphological, and optoelectronic properties of sprayed cadmium based transparent conducting oxide

$
0
0
Publication date: 30 April 2017
Source:Thin Solid Films, Volume 628
Author(s): S.P. Desai, M.P. Suryawanshi, M.A. Gaikwad, A.A. Mane, J.H. Kim, A.V. Moholkar
The influence of thickness on the properties of cadmium oxide thin films deposited using simple and cost-effective chemical spray pyrolysis technique is studied. The maximum film of thickness 2752nm is achieved by tuning spraying parameters. The thickness dependent structural, morphological, and optoelectronic properties of CdO thin films have been investigated in detail. The microstructure of CdO thin films significantly changed from rough to smooth and further to rougher surface with increase in film thickness. This behavior has been further confirmed from water contact angle measurement. The optical studies show that the direct band gap energy values ranging between 2.23 and 2.46eV. The Hall effect measurement indicates that all the films exhibit n-type semiconducting behavior with their electrical resistivity lies in the range of 12.8×104 to 3.7×104 Ω·cm. The CdO film with thickness of 1371nm exhibited the best optoelectronics properties (transmittance of 74%, figure of merit of 18.23×103 (Ω)1, carrier concentration of 7.30×1020/cm3 and mobility of 23.11cm2/Vs) among all the films.


Viewing all articles
Browse latest Browse all 1574

Trending Articles