Structure and electrical properties of sputtered Cu2−xTe films (0 ≤ x ≤ 1)

Publication date: 1 May 2018
Source:Thin Solid Films, Volume 653
Author(s): J.U. Salmón Gamboa, Marius Ramírez Cardona, M.A. Hernández Landaverde, S.J. Jiménez Sandoval
Radio frequency sputtering was used to grow copper telluride films from targets fabricated by cold pressing mixtures of copper and tellurium powders. Through this method, Cu2−xTe targets and films with 0 ≤ x ≤ 1 in nominal composition were elaborated. X-ray diffraction showed that the films comprised mixtures of various copper telluride phases. However, dominant phases resulted, in most cases, depending on the target nominal composition and on the substrate temperature. The temperatures employed varied between room temperature and 350 °C. In the specific cases of growths at 100 °C from the target with nominal composition [Cu]/[Te] = 1, and at 200 °C from the [Cu]/[Te] = 1.5 target, nearly single phases of CuTe and Cu7Te5 were obtained, respectively. Through Hall effect measurements the resistivity, free carrier density and mobility were determined as a function of target composition and substrate temperature.